A dense alumina refractory and a chrome refractory had the lowest meltline corrosion rate in the iron phosphate melts, whereas the corrosion rate of silica, zircon, and aluminazirconiasilica(AZS) refractories was somewhat high.

• 在铁磷模拟核废料熔体中 ,致密氧化铝和氧化铬耐火材料有最低的熔线腐蚀速度 ,二氧化硅、锆英石和 AZS耐火材料的腐蚀速度比较高。