Abstract The main reason of heading crack for BOF producing bearing steel is analyzed.The result shows that the high hydrogen content and gas generated by it lead to surface pinholes in steel.

• 摘要 分析了造成转炉生产轴承钢顶锻不合格的主要原因，指出了钢中氢高且生成气体而导致表面针孔。