您要查找的是不是:
- Composite phosphate coating 复合磷化膜
- An uniform zinc phosphate coating was fabricated on the surface of AZ91D Mg alloy. 在AZ91D镁合金表面制备了细致均匀的锌系复合磷化膜。
- At the same time we discovered that composite phosphate, hetero-ascorbic acid nicotinamied along with cigarette amide possess an evident shelte... 同时发现,复合磷酸盐与异抗坏血酸钠、烟酰胺对鲜肉有明显护色作用,涂膜显著降低汁液流失量。
- The process and parameters of chemical precipitation to treat phosphate coating wastewater is presented in this paper. 作者提出了用化学沉淀法处理磷化废水的工艺流程和技术参数。
- The wire have been phosphate coated and uniformly,coincidently. 钢丝经磷化处理;且磷化层均匀;一致.
- The BR-III-B phosphate coating agent is a phosphorizing liquid that may be applied under both ambient and higher temperature. BR-B皮膜剂是一种既适用于常温又能在加温下使用的磷化液。
- The wire have been phosphate coated and uniformly, coincidently. 钢丝经磷化处理,且磷化层均匀,一致。
- According to the multiple actors in orthogonal experiment, the optimal tender formula of braised goose series handy food was:the papain 0.04%, lime chloride 3%, composite phosphate 0.4%. 采用正交试验设计得出酱香鹅最佳嫩化配方为:木瓜蛋白酶浓度0.;04%25;氯化钙浓度3%25、复合磷酸盐浓度0
- The results showed that modified phosphatic coating layer could effectively inhibited oxidation of C/C composite braking material at simulated aircraft stopping factors. 涂层炭/炭复合材料试样在高温空气气氛中进行热震试验和恒温氧化试验,结果表明改性磷酸盐涂层对炭/炭复合材料具有良好的氧化抑制作用。
- In particular attention was payed on the effect of factors sush as the content of REC,pH,and time on the morphology,thichness as well as corrosion resistance of the phosphate coating. 探讨了在硝酸盐-锌系磷化过程中稀土化合物、溶液酸碱度、时间对磷化膜外观、膜重和耐蚀性的影响。
- Development of new technology of coating layer on actual wrought magnesium alloy structure, for example micro-arc oxidation, anodic oxidation, and phosphate coating, should be emphasized. 指出应该加强对实际的变形镁合金构件的表面改性技术的开发,尤其是对试样研究较多的微弧氧化法、阳极氧化法和磷化。
- The article mainly focused on analyzing the cause of formation of phosphate coating film speckles on the outer ring of bearings in the manufacturing progress of railway bearing in Xibei Bearing Co. 摘要针对西北轴承股份有限公司铁路轴承外套在生产过程中,突然出现磷化膜颜色深浅不均匀的云彩状花斑,进行成因分析。
- Results show that the targeted composite phosphating coaling was black and had compact needle-hole-like morphology. 结果表明:复合磷化膜呈黑色、细密针孔状结构;
- Through a large number of experiments,the best technological parameters for this composite phosphatizing solution are decided. 结果表明,耐磨复合磷化克服了以往磷化工艺的不足。
- A composite phosphatizing solution is developed according to the mechanism of phosphatizing film forming and the best prescription of phosphatizing solution is designed. 依据磷化的成膜机理,设计了复合磷化液的配方,并确定出磷化液的最佳配方。
- In order to improve quality of the phosphating coat and extend lifetime of the phosphating solution, the problem of unusual sediment is studied. 摘要为了提高磷化膜质量,延长磷化液使用寿命,针对异常沉渣这一问题,进行了长期的试验研究。
- iron-manganese phosphate coating 磷酸铁锰处理膜
- Keywords composite phosphate;boneless and massive Ham; 复合磷酸盐;骨块状火腿;
- The effect of technological parameters on phosphatizing coating is also investigated such as time,temperature,and acid rate and etc,. 研究了时间、温度、酸比等工艺参数对磷化成膜的影响,通过实验确定出此种耐磨复合磷化的最佳工艺。
- Keywords iridescence;tumbling;cooking;salt;composite phosphate; 彩虹色斑点;滚揉;煮制;食盐;复合磷酸盐;