However, the flaking cracks in low carbon high alloy steel are initiated in subsurface stratum, which induces no apparent effect for corrosion on flaking.
英
美
- 低碳高合金钢剥落裂纹起源于亚表层,腐蚀对其裂纹形成乃至剥落无明显作用。