Instead, it was found that the corrosion fatigue and stress corrosion were the main reasons for the cracking of the tubesheet.
英
美
在腐蚀介质(水蒸气、氧、油浆中的硫)及拉应力的共同作用下,又使管板受到应力腐蚀。