- The results showed that, when amorphous Cr Si Ni N films were heated up, crystallization phase CrSi 2 was formed. 结果表明 ,非晶Cr Si Ni N薄膜在加热过程中 ,将析出晶化相CrSi2 ;
- Therma fatigue behaviors of Ni base alloy chromium carbide composite coating made by a vacuum fusion sintering method are discussed in this paper. 研究了用真空熔烧法制得的镍基合金-碳化铬复合涂层的热疲劳行为。
- The wear test of Ni based alloy-Cr/WC composite coating without lubrication is carried on a MM-200 pin-on disc wear tester and study wear-resisting property. 在MM-200型销盘式磨擦磨损实验机上,对Ni基Cr/WC复合涂层进行了无润滑的干磨擦磨损试验,研究其磨损特性。
- The technical parameters and production process of the combine roller made from high Ni Cr cast iron by centrifugal casting were intruduced in detail. 详细介绍了离心铸造高镍铬铸铁复合辊套内外层金属铸造工艺参数及整个铸造生产过程。
- Abstract： Therma fatigue behaviors of Ni base alloy-chromium carbide composite coating m ad e by a vacuum fusion sintering method are discussed in this paper. 摘 要： 研究了用真空熔烧法制得的镍基合金-碳化铬复合涂层的热疲劳行为。
- Distribution of elements content (As、Ni、Cr、Mn) in steel's section were analyzed by X-ray Fluorescence Spectrometry (XRF). 应用X荧光光谱法分析了螺栓圆钢截面砷、镍、铬、锰元素的分布。
- The results indicate that every performance of melting range reaches or surpasses respective performance of related cobalt alloy and Ni Cr alloy. 结果表明，熔接区的各项性能均达到和超过相关的钴合金及镍铬高温合金的各自性能。
- Under the same heating rate, the crystallization temperature of Ni P UFD composite coating is lower than that of Ni P coating, while the peak temperature of the two electroless coating are well matched. 在相同的加热速率下 ,Ni P UFD复合镀层晶化的起始温度均低于Ni P镀层 ,但峰值温度与Ni P镀层相当 ;
- In order to develop new generation monolayer brazing CBN (cubic boron nitride) grinding wheels, two types of active filler alloys (Ni Cr and Ag Cu Ti) were tested in vacuum furnace. 为研制我国新一代单层钎焊CBN(立方氮化硼 )磨料砂轮 ,尝试Ni-Cr和Ag -Cu-Ti两种活性钎料 ,在真空炉中钎焊。
- Abstract By addition of a reactant with stoichiometric ingredient of Ti and B to molten Al Si alloy,a particulate reinfaced cast TiB 2/Al Si composite by in situ reaction has been achieved. 在铝硅合金熔体中加入Ti和B成理想配比的反应剂，原位生成颗粒增强铸造复合材料TiB2/Al?Si。
- Ni base alloy/WC composite coating 镍基合金／WC复合涂层
- The paper present the new developments of Ni-W coat, Ni-W-B coat, tungsten composite coat and tungsten brush coat etc. 介绍了镍钨镀层、镍钨硼(磷)镀层、含钨复合镀层和含钨电刷镀镀层等的研究与开发的近期进展。
- SiC p/Al Si composites were studied by means of conventional TEM. The conception of "interfacial Si" was proposed. 采用TEM 研究了SiC/Al?Si 复合材料， 提出了“界面Si”的概念。
- The results show that multiplayer Ni-Cr 2O 3 composite coating have a strong wear resistance. 结果表明 ,电刷镀多层Ni-Cr2 O3复合镀层具有良好的耐磨性。
- Based on this work, interlayer shielding composite coating gains more SE than 52dB between 3OMHz-I000MHz planewave. 在此基础上制备的层状复合屏蔽涂料获得了30MHz-1000MHz频段SE分贝值超过52dB的成果。
- Microstructure of the ceramal composite coating was characterized by SEM,XRD and EDS. 利用SEM、XRD和EDS等分析了涂层的显微组织和相组成;
- The ceria content of the nanocomposite coating is more than that of the micron composite coating. 纳米复合涂层中氧化铈的含量高于微米复合涂层中的氧化铈含量;
- The anti-cracking performence of the composite coating with nonwoven fabric was discussed in the article. 对用非织造布增强的复合腻子层的抗裂纹性能进行了研究。
- Using stiring and ultrasonic dispersing,nano-SiO_2 composite coating was obtained by adding nano-SiO_2 into varnish. 在机械搅拌和超声场的共同作用下,将改性纳米二氧化硅分散到醇酸清漆中,获得纳米二氧化硅复合涂料。
- Arc sprayed aluminium composite coating can increase the service life of reaction caldron up to the design life. 采用电弧喷涂铝复合涂层来解决反应釜的腐蚀问题，可使其达到或超过设计寿命。