您要查找的是不是:
- The results show that sericin could be directly coated on the oxidized cotton fiber without any other reagent and form a covalence bond between amido group and aldehyde group. 研究结果表明,不需要添加其他试剂,丝胶可以直接涂覆于氧化棉纤维上,并生成席夫碱结合键;
- Keywords oxidized cotton fiber;fibroin;imine covalence;dialdehyde cellulose; 氧化棉纤维;丝素蛋白;亚胺结构;二醛纤维素;
- Keywords Oxidized cotton fiber;Sericin;Weight gain;Breaking strength; 氧化棉纤维;丝胶;增重率;断裂强度;
- Oxidized cotton fiber 氧化棉纤维
- selective oxidized cotton fiber 选择性氧化棉纤维
- Structure and Properties of the Oxidized Cotton Fibers Treated by Keratin Solution 氧化棉纤维经角蛋白溶液处理后的结构及性能研究
- Used for testing the cotton fiber length. 用于测量棉纤维的长度。
- Used for testing cotton fiber's micronaire value. 用于测定棉纤维的马克隆值。
- Used for testing cotton fiber’s micronaire v... 用于测定棉纤维的马克隆值。
- Cotton fiber is a seed-hair consisting of a single cell. 棉花纤维是单一细胞的种子纤维。
- oxidized cotton fibers 氧化棉纤维
- Cotton fiber is an important raw mate-rial for industry. 棉纤维是重要的纺织工业原料。
- Reactive dyes were used to dye the HPB-NH2 grafted oxidized cotton fabrics and their dyeing properties were tested. 采用活性染料对HPB-NH2接枝氧化棉织物进行染色试验并测试其染色性能。
- Selectively oxidized with NaIO4,cotton fibers were treated with sericin solution.The structure and properties of cotton fibers coated with sericin were studied. 采用高碘酸钠对棉纤维进行选择性氧化,再利用丝胶溶液对棉纤维进行处理,使丝胶涂覆于棉纤维上,并对经丝胶处理后的棉纤维结构和性能进行了测试分析。
- Light microscopy has also been useful in studies on the secondary wall of the cotton fiber. 光学显微镜还可以用来研究棉纤维的次生层。
- Results demonstrated that HPB-NH2 grafted oxidized cotton fabrics displayed markedly enhanced color yield, and the washing fastness, rubbing fastness and leveling properties were satisfactory. 结果表明,HPB-NH2接枝氧化棉织物的得色量显著提高,耐摩擦色牢度、耐洗色牢度以及匀染性能都令人满意。
- The coat is made of fabric woven from cotton fibers. 这件衣服是由棉纤维制成的纤维织品。
- The spinning jenny and the power loom had made it possible to turn the cotton fiber into cloth quickly. 纺纱机和动力织布机使人们能迅速将棉花纤维转变成布。
- The accumulation of biochemical components in ovule of cotton fiber mutants during the ovule development. 棉花纤维突变体胚珠发育过程中主要生化物质的积累特征。
- The breaking strength and elongation decreased as the degree of oxidation of cotton fiber increased. 氧化棉纤维的断裂强度和断裂伸长率随氧化程度的提高不断降低。