The aim of the analysis was to explain the cavitation erosion failure mechanism as a fatigue crack propagates through the tri-layered structure of a bearing.

• 对合金层为3层结构的轴承气蚀失效机理进行了分析并解释了疲劳裂纹通过由不同材料构成的3层结构的变化。