The causes of producing fine during ferromanganese-silicon cooling and crushing is analyzed. The measures and methods are put forward to prevent and reduce degradation index during crushing.
英
美
- 对锰硅合金冷凝及破碎为规格粒度过程中产生粉末的原因进行了分析,提出了防止和降低破粉率的措施和方法。