The fracture failure would occur in nodular iron crankshafts due to the over-shallow and non-uniform thickness of nitriding layer.

• 球铁曲轴常常由于渗氮层薄、质量不稳定而引起断裂失效,本课题研究了球铁曲轴加氧渗氮工艺。