The reason of fracture failure of the zinc coating dislo-cation-tooth circlet was analyzed in detail by means of metallographicmicroscope, SEM, energy spectrum and analyzing the hydrogen content.
英
美
- 本文较详尽地介绍和分析了镀锌错齿垫圈断裂失效的原因。