The results indicate that the fatigue fracture in early stage on the coupler was caused by lower silicon content, worse mechanical property and improper mechanical processing.

• 结果表明，由于联轴节硅含量太低、力学性能不好、机加工不当，导致联轴节早期疲劳断裂。