When DAIP is prepolymerized to be gellike, the impact strength can be increased to over two times, the bending strength is slightly increased, and the heat distortion temperature (HDT) is not changed basicaly.

• 当DAIP预聚至凝胶状时浇铸体的冲击强度可提高2倍多,弯曲强度也有所上升,但热变形温度(HDT)变化不大;