- The retrogradation was increased by a slower cooling rate. 慢速降温冷却也有利于增大回生程度。
- At a slow cooling rate, the size of spherulite becomes larger and more regular. 并且在慢速冷却条件下,球粒尺寸明显增大,球体更加规则。
- The formability would be influenced with the reduction of the cooling rate. 但随着冷却速度下降,易产生流淌,影响成形性。
- However,at the relatively faster cooling rate,when the tempering tempe... 快速冷却条件下,回火温度升高,强韧性下降。
- Effects of cooling rate on eutectic microstructure of Zn-(0.24Ni) alloy for hot dip galvanization were investigated. 研究了冷却速度对用于热浸镀Zn的Zn0.;24Ni合金共晶组织的影响。
- It is found that the cooling rate has great effect on oxide precipitation and growth. 计算结果表明,冷却速率对凝固过程中氧化钛的析出和长大有重要影响:冷却速率越小,氧化钛长得越大。
- The more the increasing of cooling rate or pre-deformation, the more the secondary dendrite arms are easy to coarsen. 冷却速率越大或预变形处理以后的试样在熔化过程中更容易发生二次枝晶臂之间的合并。
- The higher the cooling rate, the lager the corresponding thermal expansion changes. 降温速率越大,其相应的热膨胀系数也越大;
- The more the increase of cooling rate or pre-deformation, the more the secondary dendrite arms are easy to coarsen. 冷却速率越大或预变形处理以后的试样在熔化过程中更容易发生二次枝晶臂之间的合并。
- The influence of cooling rate on the room temperature resistivity of PTCR ceramics was studied emphatically. 着重研究降温速率对PTCR室温电阻率的影响。
- Computer simulation showed that the cooling rate of castings can be reduced by such method. 计算机模拟表明,这种工艺方法还可以降低铸件冷却速度。
- The precipitation amount of Nb(CN) particle increases firstly and then decreases at different cooling rate. 在不同冷却条件下,碳氮化铌的析出量随反应时间呈先增加后减少的趋势;
- The metallographic cooling rate was measured for the Deng Ujimqin mesosiderite using And profile ac concentration vs. 采用剖面中间浓度与镍纹石带宽度关系测定了东乌珠穆沁中铁陨石的金相冷却速率,其冷却速率介于0。
- As a result,the compressed air supply is saved greatly,its jet speed of airflow increased and the cooling rate raised. 既大大地节约供气量,又增加气流射速,提高冷却速率。
- As a result, It is found that the cooling rate has great effect on the Nb(CN) nucleation and growth. 计算结果表明:冷却速率对碳氮化铌的析出及长大有重要影响。
- In the course of formation of the labrador megacryst lapilli, the temperature and the cooling rate are the major factors controling their crystallization and growth. 托勒巴契克火山拉长石巨晶火山砾形成过程中,温度和冷却速率乃是控制其结晶生长的主导因素。
- The faster the cooling rate and the shorter the time to reach the precipitation amount peak value, the smaller are the precipita... 随着冷却速率的提高,达到析出量峰值的时间越短,析出量和析出粒子的平均直径均减小。
- Formation of large quantities of the flake perlite is closely dependent on the extremely low cooling rate before and after wire-drawing. 大量粗片状珠光体的形成与吐丝前后的冷却速度过慢等因素有关。
- The experiment shows that increasing cooling rate is advantageous to spread and graining of non-equilibrium microstructure around the primary grains. 结果表明:增加冷却速率、预变形处理和晶粒细化有利于初始凝固组织中存在的非平衡组织的分散细化。
- However, in the samples with the fast cooling rate, we observe the red shift of PL peak and radiative efficiency degradation. 然而快速降温的样品频谱峰值能量发生红移,并降低了发光效率。