- crystalline phase formation 晶相形成
- The XRD result shows that the main crystalline phase of the ceramic is mullite. 射线衍射分析结果表明,材料的主晶相为莫来石。
- DSC result shows that, crystalline phase solid-solid-transition for nylon11 is emerged at95℃. dsc谱图显示,尼龙11在95℃发生晶相固-固转变现象,而加入核-壳冲击改性剂及环氧树脂后晶相转变消失,表明了尼龙11合金不存在多晶型晶态。
- Butyryl chitosan can form cholesteric liquid crystalline phase by dissolving in more than ten solvents. 丁酸壳聚糖能溶于十多种溶剂中形成胆甾型液晶相。
- The results indicated that PTT/PBT blends were miscible in amorphous phase, while phase separated in crystalline phase. 结果表明:PTT/PBT共混体系在无定形区具有较好的相容性,但在晶区是晶相分离的。
- One of the two phases is richer and the other poorer inSnSe. The phase separation causes a decrease jn activation barrier for the formation ofZrSe_2 nucleation substrates, thereby favours the nucleation of the major crystalline phase(GeSe_2 and SnSe). 分相不仅降低了ZrSe_2核化的活化能垒,而且对GeSe_2与SnSe的成核都产生有利影响。
- Carbon steels exist in three stable crystalline phases. 碳素钢含有3种稳定的结晶状态。
- Kakali G,Parissakis G,Bouras D.A study on the burnability and the phase formation of PC clinker containing Cu oxide[J].Cem Concr Res,1996,26:1473. 侯贵华沈晓冬许仲梓.;高硅酸三钙硅酸盐水泥熟料组成及性能的研究[J]
- The influence of different ratio of raw materials on crystalline phases and unit cell parameters were studied and the formation mechanism of mullite solid solution was discussed. 探讨不同配方合成的莫来石的晶相组成、晶胞参数及带有结构缺陷的莫来石固溶体的形成机理。
- The catalysts whose main crystalline phase are (VO)2P2O7 exhibit different catalytic properties because of different precursors and activated ambience. 主体晶相同为(VO)_2P_2O_7的催化剂,因催化剂前驱体的制备方法及活化条件不同,催化性能相差悬殊;
- The relation between microstructure, phase formation, composition, magnetic properties and magnetostriction of these compounds have been discussed. 研究了这些稀土过渡金属化 合物的显微结构、均 匀范围和形成规律。
- The variation of the absorption, transmission and reflectivity of the amorphous and crystalline phase change film with the wavelength are studied. 同时,研究了晶态和非晶态相变薄膜的吸收率、透射率和反射率随波长的变化。
- The phase transition temperature and liquid crystalline phase texture of polyA were investigated by DSC, X-ray diffraction andpolarized microscopy. 聚合物的相转变温度和形态织构用DSC、X-射线衍射和偏光显微镜进行了测定和观察。
- Phase Formation of Diblock Copolymer Based on Soft Behavior of Polymer, Yumei Gong , Haiying Huang, and Tianbai He, International Symposium on Polymer Physics, 2006, Suzhou. 溶剂挥发速度对溶液浇液浇铸嵌段共聚物薄膜相行为的影响;宫玉梅,胡志军,何天白,2005年全国高分子学术论文报告会摘要集.
- A homogeneous crystalline phase that contains two or more chemical species.Both substitutional and interstitial solid solutions are possible. 包含两种或两种以上元素的均匀单相,固溶体可以以置换固溶体或间隙固溶体的形式存在。
- DTA, XRD, SEM, TEM, HREM etc. were applied to analyze the microstructure, crystalline phase and composition of the rare-earth nanometer Au catalysts. 文章借助于差热分析(DTA)、X-射线晶相分析(XRD)、扫描电子显微镜实验(SEM)、透射电子显微镜实验(TEM)、高分辨电镜(HREM)等分析手段对纳米稀土金催化剂的微观结构、晶相组成进行了表征与分析。
- Liquid crystalline phase transitions in PBA/nylon 6/H2SO4 systems were studied by Polarized Light Microscope (PLM) and Depolarized Light Intensity (DLI) technique. 本文用PLM及DLI法研究了聚对苯甲酰胺及聚对苯甲酰胺/尼龙6的硫酸溶液由液晶态转变为非液晶态过程的相转变动力学;
- APC thermotropic liquid crystalline phase transition, the texture of APC/DBP lyotropic liquid crystal and influence were studied by DSC, PLM, X-ray diffraction and SALS. 以DSC、X-ray衍射、PLM和SALS手段研究了产物的热致液晶相转变及其影响因素和溶致液晶性。
- The results show that the dominant crystalline phase is diopside.With the increasing of time, crystal percentage and crystal size of the glass-ceramics are increased.... 研究表明:钢渣微晶玻璃主晶相为透辉石,晶化时间延长导致晶体长大、晶相含量增多,抗弯强度先增大后减小。
- It is also found that boron can improve the phase formation of Laves phase compounds. 15 papers have been published in international journals, like Applied Physics Letters, Physical Review B, etc. 发现硼原子能促进相形成,从而提高化合物的磁致伸缩性能。在应用物理快报、物理评论等国际学术刊物上发表论文15篇。对发展新型廉价巨磁致伸缩材料有重要指导意义。