- Results indicated that microstructure of the ZSF alloy consists of austenite and eutectic cementite. 结果表明,ZSF合金的显微组织是奥氏体+共晶碳化物。
- The results showed : in the as-cast white iron there was the enrichment of silicon between the eutectic cementite and pearlite. 结果表明:硅在共晶渗碳体和珠光体界面处富集,少量硅进入共晶渗碳体中;
- The effect of Si on the crystal lattice parameters,lattice volume and crystal defects of the eutectic cementite in malleable cast iron has been studied by using X ray diffractometer and TEM. 采用X-射线衍射仪、透射电镜研究了可锻铸铁白口组织中硅对共晶渗碳体点阵参数、晶胞体积及晶体缺陷的影响。
- Keywords Quantitative metallography;mellable cast iron;fracture dutility;eutectic cementite;graphitizing annealing; 定量金相技术;可锻铸铁;断裂韧性;共晶渗碳体;石墨化退火;
- Keywords malleable cast iron inoculant graphitization at first stage decomposition of eutectic cementite; 可锻铸铁;孕育剂;第一阶段石墨化;共晶渗碳体分解;
- eutectic cementite 共晶渗碳体
- A eutectic mixture,solution,or alloy. 低共熔混合物,易熔质易熔的混合物,溶体或合金
- A eutectic is atx=0.147 and T=221.28K. 转熔点位置在 (0 .;72 8;2 80
- Large eutectic ledeburite is not found. 合金层中的碳化物细小、均匀、弥散,无粗大的共晶莱氏体组织。
- A eutectic mixture, solution, or alloy. 低共熔混合物,易熔质易熔的混合物,溶体或合金
- The distribution of cementite particle size displayed bimodal. 颗粒状渗碳体的尺寸呈双峰分布。
- In this work,we mainly studied the effect of free cementite in 1. 对低碳钢薄板中游离渗碳体形态与其杯突值关系进行了试验分析;对1。
- Eutectic carbide in network made white iron was britten. 共晶碳化物呈连续网状分布是白口铁脆性的根源。
- The eutectic temperature of banana pulp was measured. 利用电阻法测得了香蕉浆的共晶点温度。
- In some cases, manufacturers are unaware of the eutectic point. 在一些案例里,生产商不知道产品的共晶点。
- That's a eutectic mixture. 那是低共熔混合物。
- Thermal expansion of cementite and thermoelastic stresses in white cast iron . pdf 提供几篇相关资料,不知道有没有人需要。
- The main area of initiation is pinetree carbide and eutectic carbide. 裂纹萌生地主要为:枝晶碳化物和复式碳化物。
- A mixture of ferrite and cementite forming distinct layers or bands in slowly cooled carbon steels. 光体,珠铁在慢慢冷却的碳合金中的层状铁素体和碳素体的混合物
- The main causes which lead to tensile abnormal fracture of SWRH82B steel rods are the network cementite sod the big brittle inclusion. 摘要通过对SWRH82B盘条的拉伸断口进行分析,认为网状渗碳体和大颗粒脆性夹杂物等缺陷是引起断口异常的主要原因。