- EFFECT OF Si ON HOT DIP ALUMINUM COATING AND MECHANISM 热镀铝中硅的影响及其作用机制
- hot dip aluminum coating 热浸镀铝层
- Study of Hot Dipping Aluminum Coating and Water-Based Promotion Flux 热浸镀铝工艺及水溶液助镀剂的研究
- The effects of aluminum bath temperature, immersion time and silicon content on hot dip aluminum for HT200 are studied. 研究了热浸温度、时间及硅含量对HT200热浸渗铝的影响。
- Experiment results showed that the process of Hot Dip Aluminum and complex Boronisation on the A3 surface is feasible, it had a continuous layer between diffusion layer and matrix and a better hardness gradient. 试验表明 :A3钢表面浸镀扩散渗铝复合渗硼工艺可行 ,渗层与基体形成了连续的扩散层 ,并且具有良好的硬度梯度。
- Keywords hot dip aluminum （HDA）;dip diffusion aluminum;oxidation resistance at high-temperature;microstructure; 热浸镀铝（HDA）;浸扩铝;高温氧化性;微观组织;
- Bright hot dip aluminum plating from bath covered with no molten salt-A new process for environmentally friendly aluminum plating 钢铁件无熔盐覆盖光亮热浸镀铝-一种无污染镀铝新工艺
- A hot dip Zn 5%Al RE coating on high carbon steel wire is tested. 试验了在高碳钢丝表面上热浸镀Zn 5%25Al RE合金层。
- hot dip aluminum 热浸镀铝
- hot dip aluminum (HDA) 热浸镀铝（HDA）
- hot dip aluminum plating 热浸镀铝
- Corrosion Behaviors of Hot Dipping Aluminum Steel in Hydrogen Sulfide Solutions 渗铝钢在硫化氢盐水体系中的腐蚀研究
- The technique of hot dip Zn-Ni alloy coating is an effective method for solving the reactive steel problem in hot dip galvanizing. 热浸锌镍合金镀层技术是解决活性钢热镀锌问题的有效方法。
- Atl-5A/dm aluminum coating is dense and uniform, especially at 2.5A/dm . 在电流密度为1-5A/dm~2时得到的镀层致密均匀，其中2.;5A/dm~2时晶粒最细。
- The effect of Ni content in Zn bath on thickness of hot dip galvanized coating was studied using SEM. 应用SEM、EPMA等方法研究了锌浴中镍含量对热浸锌镀层厚度的影响，试验结果表明：当锌浴中镍含量小于0.;12%25 (wt)时，镀层随镍含量增加而减薄；
- The tensile properties and corrosion resistance of hot dip 55%Al Zn alloy coating steel are investigated. 研究了热浸镀 5 5%25Al Zn合金镀层钢的室温拉伸性能和耐蚀性能。
- The surface morphology and composition of Zn 5%Al RE coating hot dip plated on alloy steel wire was analyzed by means of metallography,SEM and EPMA. 本文采用金相显微镜、扫描电镜和能谱仪等设备分析了在Zn?5%25 Al?RE合金溶液中热浸镀中碳钢丝表面的组织形貌和成分。
- The hot dip Zn Ni alloy coating provides good anticorrosion performance. Two kinds of materials, Q235 and Q345 used for galvanizing Zn and Zn Ni alloy. 对Q2 35和Q345两种材料表面热浸镀纯Zn和Zn Ni合金 ,研究Ni对热镀锌耐蚀性的影响。
- By way of experiment, the new invention of aluminum coating was tried out on a smaller telescope disk belonging to the same observatory. 作为实验，新发明的涂铝工艺被试用于该天文台的另一架较小的望远镜的圆面上。
- The Annealing Furnace is a key Equipment for any Hot Dip Galvanizing Line. 对于任何连续热镀锌线退火炉都是关键设备。