- A foresaid structure made ASA had high notched Izod impact strength which was as high as 33kJ/m2. 上述结构赋予ASA以高抗冲性能,其缺口冲击强度最高可达33 kJ/m2。
- It has been found that the notched Izod impact strength of the blend first decreased slightly and then increased with the addition of UFPR. 研究发现,随粉末橡胶用量增大,共混物的冲击强度先有所降低然后逐渐上升。
- The notched Izod impact strength of alloy increases with the increasing of EMG content in the condition of keeping other mechanical properties. 而随着EMG含量的增加,材料的冲击强度显著提高,且其它的力学性能基本保持不变。
- When EMG was 9 phr, the notched Izod impact strength of the prepared alloy with high rigid, high toughness was 5.5 times as that of PPS. 当EMG含量为9份时;制备的高刚性、高韧性合金在保持其它力学性能基本不变的情况下其冲击强度提高了4.;5倍;
- When the total content of SBS and MBS was kept unchanged, the notched Izod impact strength of PVC/SBS/MBS blend increased with the increase of the content of MBS, and the transparency of the blend... 当SBS和MBS的总量不变时,随着MBS相对含量的增加,共混体系的缺口冲击强度逐渐增加,透光率在m(MBS)/m(SBS)=20/80时达到最大值,光学透明性能最好。
- notched Izod impact strength 缺口冲击强度
- The Izod impact strength, the bending strength and tensile strength were tested. 同时,测试了该材料的冲击强度、弯曲强度和拉伸强度。
- With the content of 5%wt ultrafine calcium carbonate, tensile strength of PP is 33.68MPa, tensile modulus is 1.38GPa, izod impact strength is 9,38KJ/m2. 超细碳酸钙改性聚丙烯时,在5%25wt左右力学性能达到最佳,拉伸强度可以达到33.;68MPa,弹性模量可以达到1
- Theshrinkage rate is decreased by 25%and the izod impact strength of the composite isincreased by 13.8%.Which is demonstrated by examining the broken surface of specimen withSEM. 冲击强度提高了13.;8%25,同时填充体系的成型收缩率较ABS下降了25%25。
- When the content of the COPA is 4%, the blends have the maximum izod impact strength and the tensile strength is nearly unchanged, POM/COPA blends have better mechanical properties. 当COPA含量为4%25时,共混物缺口冲击强度达到最大值,拉伸强度几乎不变,POM/COPA具有较理想的综合力学性能。
- It was incorporated into PVC with barium stearate,and the heat stability and mechanical property were comprehensively studied by Congo red method,Tension test and izod impact strength test. 并将它与硬脂酸钡复配添加到聚氯乙稀(PVC)中,通过刚果红试纸法、拉伸试验及冲击试验等多种方法对其PVC复配系统的热稳定性能及力学性能进行了综合研究,并确定了复配的最佳用量。
- The dependence of properties on the amount of the prepolymeric activator was also examined.It was shown that Izod impact strength of the material containing 8% prepolymer was the best. 讨论了各种因素对制备过程的影响,并测试了制品性能与预聚作用量的关系,当预聚作用量为聚合作重量的8%25时,材料缺口冲击强度最高。
- Plastics--Determination of izod impact strength 塑料悬臂梁冲击试验方法
- The Izod notched impact strength of PMMA modified by ACR increased by 42.42% when the ACR mass fraction was 5%. 当ACR质量分数为5%25时,改性PMMA的缺口冲击强度比未改性的提高了42.;42%25。
- Standard Test Method for Determining the Izod Impact strength of Plastics 塑料冲击强度测定的标准试验方法
- Testing method for izod impact strength of glass fiber reinforced plastics 纤维增强塑料悬臂梁冲击试验方法
- Determination of izod impact resistance. 英文名称: Styrene plastics.
- Keywords Nylon 6;compatibilizer;blend;Izod impact strength;toughening; 尼龙6;增容剂;共混合金;缺口冲击强度;增韧;
- The results showed the Izod notched impact strength of the modified PMMA increased with the increase of the content of ACR, while the tensile strength and bending strength decreased. 结果表明,随着ACR用量的增加,改性PMMA的缺口冲击强度不断增加,而拉伸强度和弯曲强度则成下降趋势。
- Keywords toughening;Izod impact strength;fracture surface;crystallite morphology; 增韧;缺口冲击强度;断裂形貌;结晶形态;