- slow strain tensile testing 慢应变速率拉伸
- Hydrogen embrittlement of 2205 duplex stainless steel has been evaluated using electrochemical permeation measurement, hydrogen microprint technique and slow strain rate tensile test in this study. 摘要本实验主要利用电化学氢渗透量测、氢原子微印技术及慢速率拉伸试验,针对2205双相不?钢的氢脆性与氢原子扩散方式的关系进行探讨。
- Stress corrosion crack (SCC) susceptibility of titanium alloy TA7 in methanol and hydrochloric acid-methanol solutions was studied by slow strain rate tensile test (SSRT), SEM and optical photography. 采用慢应变速率试验,辅以扫描电镜、金相观察等分析测试技术,研究了钛合金TA7在甲醇、盐酸-甲醇溶液中的应力腐蚀敏感性。
- slow strain rate tensile test 慢应变速率拉伸试验
- 9.Hydrogen embrittlement of 2205 duplex stainless steel has been evaluated using electrochemical permeation measurement, hydrogen microprint technique and slow strain rate tensile test in this study. 摘要本实验主要利用电化学氢渗透量测、氢原子微印技术及慢速率拉伸试验,针对2205双相不?钢的氢脆性与氢原子扩散方式的关系进行探讨。
- 8.Hydrogen embrittlement of 2205 duplex stainless steel has been evaluated using electrochemical permeation measurement, hydrogen microprint technique and slow strain rate tensile test in this study. 摘要本实验主要利用电化学氢渗透量测、氢原子微印技术及慢速率拉伸试验,针对2205双相不?钢的氢脆性与氢原子扩散方式的关系进行探讨。
- 6.Hydrogen embrittlement of 2205 duplex stainless steel has been evaluated using electrochemical permeation measurement, hydrogen microprint technique and slow strain rate tensile test in this study. 摘要本实验主要利用电化学氢渗透量测、氢原子微印技术及慢速率拉伸试验,针对2205双相不?钢的氢脆性与氢原子扩散方式的关系进行探讨。
- Combined by the fracture sufaces analysis, the slow strain rate tensile behaviour of an aviation organic glass in air and vapours of different solvents was investigated. 本文对三号航空有机玻璃在不同介质气氛中的缓慢拉伸行为进行了研究,并对断口的形貌进行细致的观察。
- The diffuse necking and localized necking in the tensile testing of sheet is proved through reseau strain analysis. 通过拉伸过程应变网格分析,验证了薄板拉伸分散性失稳和集中性失稳的存在。
- The cruciform biaxial tensile test is an effective and practical method to realize the process of complex strain paths. 十字形双向拉伸是实现复杂加载路径有效实用的试验方法。
- The mechanical property of AZ31 magnesium alloy rolling sheet under different temperatures and strain rates was studied through uniaxial tensile test. 通过单向拉伸试验研究了AZ31镁合金轧制板在不同温度和应变速率下的力学性能。
- The stress corrosion cracking (SCC) behaviour of 7075 aluminum alloy was studied using slow strain rate test (SSRT) technique. 采用慢应变速率试验(SSRT)研究了7075铝合金的应力腐蚀行为。
- The strain hardening behaviour of five TWIP steels with different Mn content was investigated by static tensile test and metallography. 采用静态拉伸、金相组织观察方法研究了5种不同锰含量的TWIP钢的拉伸应变硬化行为。
- Abstract The strain hardening behaviour of five TWIP steels with different Mn content was investigated by static tensile test and metallography. 摘要 采用静态拉伸、金相组织观察方法研究了5种不同锰含量的TWIP钢的拉伸应变硬化行为。
- The stress corrosion cracking(SCC)behavior of X70 steel welded joint was investigated in a near-neutral pH solution by fluctuant slow strain rate test(F-SSRT). 研究了波动频率对X70管线钢焊接接头在阴极电位下的近中性介质中慢应变速率应力腐蚀开裂(SCC)行为。
- ABS samples of physical aging and strain aging were studied by universal tensile test machine and differential scanning calorimeter(DSC). 用万能拉伸实验机和差示扫描量热仪(DSC)对物理老化和应变老化的ABS试样进行研究。
- Calculate the free point by tensile test using electric logging equipment. 用电测设备做拉伸试验算卡点。
- Large strain tensile properties of Polycarbonate/acrylonitrile butadiene styrene (PC/ABS) polymer were experimentally investigated at different environmental temperatures in this paper. 摘要本文对聚碳酸酯(PC)和丙烯腈丁二烯苯乙烯(ABS)的合金(PC/ABS)高分子材料不同环境温度下的拉伸性能进行了试验研究。
- The experiment method includes the slow strain rate test and constant K tension test for the crack propagation.In addition, it is also attested from the microstructure and electrochemical properties. 试验方法包含有定速率拉伸和定荷重量测裂缝成长,另外也从显微组织和电化学等特性加以佐证。
- Tensile tests and slow srain rate tests(SSRT) are used to investigate the mechanical behaviors of X70 pipeline steel after electrochemical hydroge charging. 应用拉伸试验和慢拉伸试验,研究X70管线钢电化学充氢后材料拉伸性能的变化。