- The Effect of the Electrolyses Plating Quality on the Stress Corrosion Fracture of Kovar Alloy 金属应力腐蚀断裂与其保护层质量的关系
- stress corrosion fracture 应力腐蚀破断,应力腐蚀断裂
- The stress corrosion mechanism in mixed solutions was studied based on the metallographic observations of scanning fracture shapes and crack extension direction. 根据扫描断口形貌和裂纹扩展途径的金相观察,还探讨了在混合溶液中的应力腐蚀机制。
- The rupture reasons of tube joint weld of the stainless steel pressure meter are analyzed.It is characteristic of stress corrosion cracking and inter granular fracture. 分析了不锈钢压力表管接头焊缝开裂的原因，认为此种开裂具有应力腐蚀开裂、沿晶断裂特征。
- This metal defect is known as stress corrosion cracking. 其金属缺陷就称为应力锈蚀腐蚀裂纹。
- The coupling agent may protect the interface against stress corrosion by water. 偶联剂可保护界面免受水的应力侵蚀。
- The stress corrosion crack causes of the reboiler cylinder served in sulphur removing system were analyzed by chemical composition,microstructure,fracture appearance and EDS of corrosion products. 采用化学成分、金相组织、断口形貌及腐蚀产物的能谱分析等方法分析了脱硫系统塔底重沸器产生裂纹的原因。
- Variations in tensile,fracture toughness and stress corrosion resistance properties were studied through the prestretching plates of different temper 7B04 new type aluminium alloys. 研究了新型的7B04铝合金预拉伸厚板在不同热处理状态的拉伸性能、断裂韧性和应力腐蚀性能的变化。
- Many studies in the related area of stress corrosion or subcritical crack growth use simplified test systems. 许多有关应力腐蚀或亚临界裂纹发展领域的研究使用了简化的试验系统。
- The problem of serious stress corrosion existed in sour water tank in sour water striping unit of sulphur workshop was analyzed. 对硫磺车间的酸性水汽提装置中的酸性水罐存在的严重应力腐蚀问题进行了分析。
- Carbon steel -- Very good mechanical properties; good resistance to stress corrosion and sulfides. 碳钢--具有很好的机械特性;良好的抗金属超应力腐蚀的能力和抗硫化物腐蚀的能力。
- Intergranular stress corrosion cracking behavior of austenitic steels on hydrogenated high-temperature. 奥氏体钢在高温氢化物中的晶间应力腐蚀开裂性能。
- stress corrosion cracking fracture 应力腐蚀开裂
- The analysis results indicated that the H_2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明,法兰断裂是由液化气中的H2S所引起的应力腐蚀开裂。
- The analysis results indicated that the H2S in the LPG caused sulfide stress corrosion cracking (SSCC) of the flange. 分析结果表明，法兰断裂是由液化气中的H2S所引起的应力腐蚀并裂。
- The results indicate that the cracks on the wainscot of gasoline tank were stress corrosion cracks. 两批油箱壁板在加工完成后,放置一段时间后出现裂纹。
- The results show that the cracking of the pipe is a kind of stress corrosion cracking (SCC). 分析结果表明，高压油管的开裂是应力腐蚀开裂造成的。
- Stress corrosion manifests itself as a crack in the metal not necessary accompanied by obvious corrosion. 应力锈蚀腐蚀会显现出金属裂纹而不一定会有明显的锈蚀腐蚀。
- Stress corrosion cracking occurs in both aluminum and magnesium alloys as well as steel. 铝和镁合金以及钢都会发生应力锈蚀腐蚀的破裂。
- Relationship between yield strength and near-neutral pH stress corrosion cracking resistance of pipeline steels-an effect of microstructure. 管道钢的屈服强度和抗近中性pH应力腐蚀开裂间的关系-显微结构的影响。